Light-reflective material and light source device using the same

ABSTRACT

There is provided a light-reflective material with which light reflectance can be efficiently increased and brightness of a flat light source can be improved without increasing the number of components. This light-reflective material comprises a laminate formed by partly bonding at least two white plastic films  2  while holding space  3.  Preferably, the white plastic films  2  are partly bonded as a laminate while holding space  3  by an adhesion layer formed partly on the white plastic film  2  surface or an adhesion layer  4  that partly has projections  5  and is formed on the white plastic film  2  surface.

BACKGROUND OF THE INVENTION

[0001] The present invention relates to a light-reflective material used as a light-reflection member in a backlight of various display devices such as a liquid crystal display, illuminated signboard, lighting equipment and so forth, and it relates to a light-source device using the same.

[0002] Conventionally, as a flat light source that lights from the back face of a signboard, a display board or the like, a plurality of rod-like light sources such as fluorescent lamps are arranged and a diffusion board, a diffusion sheet or a diffusion material formed by a combination thereof is disposed on the front face of the light source, and a light-reflective material is disposed in the back of the light source. In addition to such a backlight called a direct type, flat light sources called an edge-light type backlight, in which a lamp such as a cold-cathode tube is disposed at an end portion of a transparent plate called a light guide plate, are used for multiple purposes such as a liquid crystal display or the like. In these flat light sources, a light-reflective material is wound to the lamp or stacked on a surface opposite of a light-emitting surface of the light guide plate. As the light-reflective material for flat light sources, a white plastic film in which a white pigment is mixed in a synthetic resin or a multiplicity of fine holes are generated in the synthetic resin is used.

[0003] In order to increase brightness of the flat light source, an attempt of increasing the light reflectance of the aforementioned light-reflective material is generally conducted in addition to a method of increasing brightness of a light source such as a fluorescent light and a method of increasing transmittance of a diffusion material or the like. As a method of increasing the light reflectance of the light-reflective material, a method of stacking a plurality of white plastic films or a method of increasing the thickness of the film itself is employed.

[0004] However, when films are stacked to increase the light reflectance, the number of components of the flat light source is increased. Therefore, a problem arises that excessive labor is required for each component when the light-reflective material is processed into an appropriate shape as required or wound to a lamp, for example. Meanwhile, the method of increasing the thickness of the film itself to increase the light reflectance is also undesirable since flexibility may be deteriorated when the light-reflective material is processed into an appropriate shape as required or wound to a lamp. Further, although its cause is not clear but, when the thickness of the film itself is increased to increase the light reflectance, the increase rate of the light reflectance is lower than when the films are stacked to increase the light reflectance even though materials of the white plastic film and the total thickness are the same.

SUMMARY OF THE INVENTION

[0005] Accordingly, an object of the present invention is to increase light reflectance of a light-reflective material efficiently and to improve brightness of a flat light source without increasing the number of components to be incorporated into the flat light source. Another object of the present invention is to provide a light-reflective material having excellent flexibility as well as excellent processability and workability when incorporated into a flat light source or processed.

[0006] In order to achieve the above objects, the inventors of the present invention examined a case where the thickness of a light-reflective material is increased by not simply stacking white plastic films, but integrally bonding them. However, when the thickness of the light-reflective material is increased simply by integrally bonding the films, a new problem arose that the increase rate of the light reflectance was lower than when films were simply stacked. As a result of further assiduous studies, they found that the increase rate of the light reflectance was deteriorated since the whole surfaces were bonded to produce one body of white plastic films and that the light reflectance was significantly increased when a predetermined air layer was provided between the bonded white plastic films, and thus accomplished the present invention.

[0007] Specifically, the light-reflective material of the present invention comprises a laminate formed by partly bonding at least two white plastic films while holding space therebetween.

[0008] Further, the light-reflective material of the present invention comprises a laminate formed by partly bonding at least two white plastic films while holding space by an adhesion layer formed partly on the white plastic film surface.

[0009] Further, the light-reflective material of the present invention comprises a laminate formed by partly bonding at least two white plastic films while holding space by an adhesion layer that partly has projections and is formed on the white plastic film surface.

[0010] Further, the light source device of the present invention adopts such a light-reflective material as its light-reflective material. The light source device may be an edge-light type light source comprising a light guide plate and at least one lamp disposed at an end of the light guide plate, or a direct type light source comprising at least one lamp arranged substantially in a plane, a light diffusion member disposed at one side of the lamp (or lamp array) and a light-reflective member disposed at another side of the lamp. In an application to the edge-light type light source, the light-reflective material of the present invention is disposed surrounding the lamp and/or an opposite side of a light-emitting surface of the light guide plate.

BRIEF DESCRIPTION OF THE DRAWINGS

[0011]FIG. 1 is a cross sectional view showing one embodiment of the light-reflective material of the present invention.

[0012]FIG. 2 is a cross sectional view showing another embodiment of the light-reflective material of the present invention.

[0013]FIG. 3 is a cross sectional view showing further another embodiment of the light-reflective material of the present invention.

[0014]FIG. 4 is a perspective view showing one example where an adhesion layer partly having projections is formed on the white plastic film surface.

[0015]FIG. 5 is a perspective view showing one example where an adhesion layer is formed partly on the white plastic film surface.

[0016]FIG. 6 shows an embodiment of a direct type light source to which the present invention is applied.

[0017]FIG. 7 shows an embodiment of an edge-light type light source to which the present invention is applied.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0018] Hereafter, the light-reflective material of the present invention will be described in detail.

[0019] The light-reflective material of the present invention comprises a laminate formed by partly bonding at least two white plastic films while holding space therebetween. As a specific constitution of partly bonding the films while holding space, such a constitution can be adopted that at least two white plastic films are partly bonded as a laminate while holding space by an adhesion layer formed partly on the white plastic film surface or that at least two white plastic films are partly bonded as a laminate while holding space by an adhesion layer that partly has projections and is formed on the white plastic film surface.

[0020] Here, as the white plastic film, a film obtained by mixing a white pigment in a synthetic resin, a film made of a synthetic resin so that a multiplicity of fine holes should be generated inside or the like can be used. Examples of the synthetic resin include general synthetic resins such as polyester resins, polyethylene resins, polystyrene resins, polypropylene resins, polyether resins, polyurethane resins, polyvinyl chloride resins, polyvinyl acetate resins, acrylic resins, epoxy resins and cellulose resins. In particular, polyester resins such as polyethylene terephthalate are preferably used. When two sheets of white plastic films are bonded directly without using adhesives, at least one of the plastic films should be thermoplastic. Further, as the white pigment, barium sulfate, titanium oxide, zinc oxide, calcium carbonate, magnesium carbonate or the like can be used. In particular, barium sulfate and titanium oxide are preferred to efficiently increase light reflectance of a white plastic film.

[0021] The thickness of the white plastic film depends on the content of the white pigment and holes contained in the white plastic film, but the range of 25 to 300 μm is preferred. When the thickness is 25 μm or greater, number of white plastic films to be laminated can be within an appropriate range to sufficiently increase the light reflectance of the light-reflective material. When the thickness is 300 μm or less, the film after processing of the light-reflective material can be wound to a lamp without any trouble or processed to an appropriate shape.

[0022] The structure of a laminate formed by partly bonding at least two white plastic films while holding space will be described below.

[0023] The light-reflective material comprising a laminate formed by partly bonding at least two white plastic films while holding space therebetween can be obtained by, for example, providing a white plastic film 2 having projections and depressions on its surface, melting tops of the projections by a solvent or heat and bringing these tops into contact with a surface of another white plastic film 2 so that the tops should be bonded by fusion to the surface of this white plastic film 2. Thus the white plastic films 2 are partly bonded as a laminate without having any other substance therebetween while holding space 3 in parts corresponding to depressions of the white plastic film 2 surface as shown in FIG. 1.

[0024] Protrusions and depressions of the plastic film can be produced by embossing, molding or the like. Although the shape, gap (distance between protrusions) and thickness of protrusions are not particularly limited so far as an appropriate space can be produced between the two plastic films, for example, the width of protrusion may be in the range of 0.1 to 10 mm, the gap may be in the range of 0.1 to 500 mm and the thickness may be in the range of 5 to 50 μm.

[0025] Alternatively, in order to partly bond at least two white plastic films as a laminate while holding space, an adhesion layer 4 may be formed partly on the white plastic film 2 surface as shown in FIG. 2 or an adhesion layer 4 partly having projections 5 may be formed on the white plastic film 2 surface as shown in FIG. 3. Here, space 3 can be held between the two white plastic films 2 by utilizing no adhesion parts of the white plastic film 2 surface or depressions of the adhesion layer 4.

[0026] As described above, the light-reflective material comprising a laminate formed by partly bonding at least two white plastic films while holding space between a gap thereof via an adhesion layer or the like as required has an excellent increase rate of light reflectance due to the existence of the space between the two white plastic films in comparison with a case where the whole surfaces of white plastic films are simply bonded. The reason why light reflectance of the light-reflective material is significantly increased when the space between two white plastic films exists is not elucidated but inferred that, in addition to diffused reflection inside the white plastic films, interface reflection on the white plastic film surface is added to the light reflectance of the whole light-reflective material.

[0027] Further, in addition to the effect of increasing the light reflectance, the space between films has action of reducing deformation due to bending or the like in the light-reflective material formed by thus laminating white plastic films so as to hold space in a gap between the two white plastic films. Consequently, even when the total thickness of the light-reflective material is increased, flexibility is not deteriorated, and thus properties of the light-reflective material required when processed into an appropriate shape as required or wound to a lamp is improved.

[0028] Here, a specific shape and size of the space having such an effect as described above are not particularly limited, but, for example, shapes such as scattered points, stripes, lattice and honeycomb can be adopted. An area ratio as high as possible to the white plastic film surface is preferred. The gap between the white plastic films is preferably in the range of 5 to 50 μm.

[0029] The light-reflective material formed by laminating at least two white plastic films via an adhesion layer can be imparted with excellent flexibility in comparison with other light-reflective materials formed by bonding white plastic films by fusion without having any other substance therebetween.

[0030] Here, an adhesive for forming an adhesion layer to bond two white plastic films is not particularly limited, but adhesives for a dry laminate or hot melt such as acrylic resins, poly urethane resins, polyester resins and polyether resins or a pressure-sensitive type adhesive called a glue can be used. When an adhesive for a dry laminate is used, it is preferable to select a two-part curing type, with which an isocyanate curing agent or the like can be appropriately used in combination. When an adhesive of a pressure-sensitive type is used, flexibility as a light-reflective material can be further improved. It is effective to impart the light-reflective material with antistatic property by employing an adhesion layer having antistaticity.

[0031] The adhesion layer formed partly on the white plastic film surface can be provided by applying an adhesive onto the white plastic film surface by screen-printing etc. in a desired shape (shape such as scattered points, stripes, lattice or honeycomb). The shape, gap, thickness and so forth of the adhesion layer are not particularly limited, and an appropriate shape, gap and thickness can be selected as required. Specifically, as the shape of the adhesion layer, the width is preferably in the range of 0.1 to 10 mm, the gap of the adhesion layer is preferably in the range of 0.1 to 500 mm and the thickness of the adhesion layer is preferably in the range of 5 to 50 μm.

[0032] The adhesion layer that partly has projections and is formed on the white plastic film surface can be formed by, for example, applying an adhesive on a mold release sheet on which grooves are formed by embossing in a shape such as scattered points, stripes, lattice or honeycomb or the like and drying the adhesive to form an adhesion layer, bonding the white plastic film surface on the adhesion layer, and transferring the adhesion layer to the white plastic film surface. Here, the shape, gap, thickness and so forth of the projections formed partly on the adhesion layer surface are not particularly limited so long as the depressions can hold space between two white plastic films, and an appropriate shape, gap and thickness can be selected as required. Specifically, as the shape of the projection, the width is preferably in the range of 0.1 to 0.4 mm, the gap of the projection is preferably in the range of 0.1 to 0.4 mm and the thickness of the projection is preferably in the range of 10 to 50 μm.

[0033] The thickness of the whole light-reflective material of the present invention depends on the thickness of the white plastic film and the adhesion layer, but is preferably 1000 μm or less, more preferably 700 μm or less. When the thickness is 1000 μm or less, good processability and workability can be achieved when the light-reflective material is wound to a lamp or processed into an appropriate shape.

[0034] As described above, the light-reflective material of the present invention comprising a laminate formed by partly bonding at least two white plastic films via an adhesion layer or the like as required while holding space therebetween can efficiently increase light reflectance, and brightness of a flat light source can be improved without increasing the number of components.

[0035] Although light-reflective materials consisting of two plastic films are illustrated in the figures, the light-reflective material of the present invention may has a laminate of three or more sheets of plastic films. In such a structure, only two plastic films may be bonded so as to have space therebetween or all of the plastic films may be bonded such that adjacent films have space therebetween.

[0036] Next, a light source device using the light-reflective material of the present invention will be explained in detail hereinafter.

[0037]FIG. 6 shows a sectional side view of an embodiment of a direct type backlight of the present invention. This light source device 60 has a structure where a plurality of rod-like lamps such as fluorescent lamps 61 are arranged in the same direction, a light reflection plate 62 is disposed under the lamps and diffusion members (63, 64) are disposed on the lamps. The light reflection plate 62 and the lamps 62 are arranged in a flame 65. The diffusion members are provided to erase a pattern of lamps and may be an opaque white resin plate, a transparent film provided with a dot-pattern (lighting curtain), a diffusion film comprising an uneven light diffusion layer formed on a transparent resin plate surface or any combination thereof. In the illustrated embodiment, an opaque white resin plate 63 and a diffusion film 64 are used in combination. In addition, an electromagnetic wave shielding film may be disposed at the upper side of the lamp 61 depending on its applications.

[0038] The reflection plate 62 of the light source device 60 is composed of a light-reflective material comprising a laminate formed by bonding at least two white plastic films so as to produce a space therebetween as afore-mentioned. Since such a light-reflective material can be treated as one sheet of a light-reflective material, good processability and workability can be obtained when it is incorporated into the light source device 60 and yet brightness equal to or more than a case stacking a plurality of light reflection plates can be achieved.

[0039] The backlight shown in FIG. 6(a) is only an example of a light source device to which the light-reflective material of the present invention can be applied. The light-reflective material of the present invention can be applied to any other kinds of light sources using a light-reflective material. Another example of the same direct type backlight is shown in FIG. 6(b), in which a bellows-like flame 66 and a light reflection plate having the same shape 67 are combined, rod-like lamps 68 are disposed in depressions of light reflection plate 67 and covered with a diffusion member such as a resin plate 69. In this backlight, the light-reflective material of the present invention is used as the light reflection plate 67. FIG. 7 shows another example of a light source device to which the present invention is applied, in which a rod-like lamp 72 is disposed at one (or both) end of a light guide plate 71, a diffusion member such as a diffusion film 73 is disposed on a light-emitting surface of the light guide plate 71 and the light reflection plate 74 is disposed on an opposite side of the light guide plate 71. In this case, the light-reflective material of the present invention is used not only for the light reflection plate 74 but also for a lamp reflector 75 which covers the lamp 72. Since the light-reflective material of the present invention has an excellent flexibility, it is incorporated into the lamp easily and exhibits a good light-shielding property as a lamp reflector. Accordingly, light emitted from the lamp 72 is introduced into the light guide plate efficiently and emitted from the light-emitting surface of the plate to bring a high brightness.

EXAMPLES

[0040] Hereafter, the present invention will be explained more specifically with reference to the following examples. In the following examples, “part” and “%” are used on a weight basis unless otherwise indicated.

Example 1

[0041] Polyethylene was laminated on wood free paper having a basis weight of 110 g/m² at a thickness of 30 μm, and cone-shaped depressions, of which each opening has an inside diameter of 0.3 mm and a depth of 20 μm, were formed by embossing at intervals of 1 mm in the length and breadth directions to prepare a mold release sheet.

[0042] 70 g/m² of an acrylic adhesive (BPS-5160: Toyo Ink Mfg. Co., Ltd.) was applied to the surface of the mold release sheet provided with the cone-shaped depressions and dried to form a pressure-sensitive type adhesion layer.

[0043] The adhesion layer surface of the mold release sheet and one surface of a white plastic film (Lumirror E60L: Toray Industries Inc.) having a thickness of 188 μm were laminated, and then the mold release sheet was peeled from the white plastic film so that the adhesion layer was transferred to the white plastic film (FIG. 4). The adhesion layer surface and one surface of another white plastic film having a thickness of 188 μm (Lumirror E60L: Toray Industries Inc.) were laminated to produce the light-reflective material of the present invention (FIG. 3).

Example 2

[0044] A UV-curable type adhesive (UV TAC-4100: Teikoku Printing Inks Mfg. Co., Ltd.) was screen-printed on one surface of a white plastic film (Lumirror E60L: Toray Industries Inc.) having a thickness of 188 μm in a lattice so that the adhesion layer had a width of 0.3 mm, a gap (one side) of 3 mm and a thickness of 20 μm, and UV-cured to form a pressure-sensitive type adhesion layer (FIG. 5).

[0045] This adhesion layer of the white plastic film and one surface of another white plastic film (Lumirror E60L: Toray Industries Inc.) having a thickness of 188 μm were laminated to produce the light-reflective material of the present invention (FIG. 2).

Comparative Example

[0046] An acrylic adhesive (BPS-5160: Toyo Ink Mfg. Co., Ltd.) was applied on a whole surface of a white plastic film (Lumirror E60L: Toray Industries Inc.) having a thickness 188 μm and dried to form a pressure-sensitive type adhesion layer having a thickness 20 μm.

[0047] This adhesion layer of the white plastic film and one surface of another white plastic film (Lumirror E60L: Toray Industries Inc.) having a thickness of 188 μm were laminated to produce a light-reflective material.

[0048] The light-reflective materials of Examples 1 and 2 and Comparative Example obtained as described above were incorporated in a surface opposite of its light-emitting surface of a light guide plate of an edge-light type backlight unit as shown in FIG. 7, and brightness (front brightness) in the normal line direction with respect to the light-emitting surface was measured. The measurement results are shown in Table 1.

[0049] The light-reflective materials of Examples 1 and 2 and Comparative Example obtained as described above were also incorporated in a direct type backlight unit as shown in FIG. 6(a) as a light refection plate, and brightness (front brightness) in the normal line direction with respect to the light-emitting surface was measured. The measurement results are also shown in Table 1.

[0050] Further, diffusion reflectances of the light-reflective materials of Examples 1 and 2 and Comparative Example were measured at 650 nm, 550 nm and 450 nm by using a spectrophotometer (UV-3101PC: Shimazu Corporation). These measurement results are also shown in Table 1. TABLE 1 Brightness (cd/m²) Edge Vertical Reflectance (%) light type 650 nm 550 nm 450 nm Example 1 422 494 96.4 96.6 96.5 Example 2 419 491 96.4 96.5 96.5 Comparative 410 480 96.2 96.3 96.1 Example

[0051] As evident from the results in Table 1, the diffusion reflectances of the light-reflective materials obtained in Examples 1 and 2 were higher with light at all measured wavelengths than the light-reflective material of Comparative Example, which was formed by bonding the whole surfaces of the two white plastic films. Brightness of the backlight unit incorporated with either of these materials of Examples 1 and 2 was also excellent.

[0052] Since the light-reflective material of the present invention comprises a laminate formed by partly bonding at least two white plastic films while holding space, light reflectance can be efficiently increased, and brightness of a flat light source can be improved without increasing the number of components. 

What is claimed is:
 1. A light-reflective material comprising a laminate formed by partly bonding at least two white plastic films while holding space therebetween.
 2. A light-reflective material comprising a laminate formed by partly bonding at least two white plastic films while holding space by an adhesion layer formed partly on the white plastic film surface.
 3. A light-reflective material comprising a laminate formed by partly bonding at least two white plastic films while holding space by an adhesion layer that partly has projections and is formed on the white plastic film surface.
 4. The light-reflective material according to any one of claims 1 to 3, wherein the dimension of the space in the thickness direction of the white plastic film is in the range of 5 to 50 μm.
 5. A light source device comprising a light guide plate, a light source disposed at least at one end of the light guide plate, and a light-reflective material disposed surrounding the light source and/or on a surface opposite of a light-emitting surface of the light guide plate, wherein the light-reflective material according to any one of claims 1 to 4 is used as the light-reflective material.
 6. A light source device comprising one or a plurality of light sources disposed substantially in a plane, a light diffusion material disposed on one side of the light sources and a light-reflective material disposed on the other side, wherein the light-reflective material according to any one of claims 1 to 4 is used as the light-reflective material. 